Synthesis and Characterization of Nanostructured (Fe۸۰Ni۲۰)۱-xCrx(x= ۰, ۴) Alloys Using Mechanical Alloying and Density Functional Theory
محل انتشار: مجله علم مواد و مهندسی ایران، دوره: 21، شماره: 2
سال انتشار: 1403
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 22
نسخه کامل این مقاله ارائه نشده است و در دسترس نمی باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJMSEI-21-2_003
تاریخ نمایه سازی: 29 اردیبهشت 1403
چکیده مقاله:
Mechanical alloying was employed to synthesize a nanostructured alloy with the chemical formula of (Fe۸۰Ni۲۰)۱-xCrx (x= ۰, ۴). The microstructural and magnetic properties of the samples were investigated using scanning electron microscopy (SEM), X-ray diffraction (XRD), energy dispersive X-ray spectroscopy (EDS), and a vibrating sample magnetometer (VSM). Additionally, theoretical calculations were performed using density functional theory (DFT) under the generalized gradient approximation (GGA). Simulations have demonstrated that an appropriate quantity of chromium (Cr) can dissolve within the BCC-Fe (Ni) structure, resulting in a favorable enhancement of the magnetic moment of the lattice. The XRD results indicated that after ۹۶ hours of milling, Fe (Ni) and Fe (Ni, Cr) with a body-centered cubic (BCC) structure were formed. With increasing milling time, the grain size decreased while the microstrain increased. The saturation magnetization (Ms) of Fe۸۰Ni۲۰ composition increased up to ۳۲ hours of milling, but further milling (up to ۹۶ h) resulted in a decrease in the saturation magnetization However, for the (Fe۸۰Ni۲۰)۹۶Cr۴ powders, milling up to ۶۴ h caused a reduction in Ms. The coercivity (Hc) trend was different and increased with longer milling times (up to ۹۶ h) for both compositions.
کلیدواژه ها:
نویسندگان
Seyed Farzad Dehghaniyan
Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran,
Shahriar Sharafi
Department of Material Science and Engineering, School of Engineering, Shahid Bahonar University of Kerman, Kerman, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :