Kinetics of thermal degradation of PMMA-based dental resins scraps
محل انتشار: نشریه آسیایی شیمی سبز، دوره: 4، شماره: 2
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 377
فایل این مقاله در 18 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_AJGC-4-2_008
تاریخ نمایه سازی: 1 مرداد 1399
چکیده مقاله:
In this work, the cross-linked PPMA-based dental resins scraps were applied to pyrolysis to recover MMA (Methyl methacrylate). Thermal degradation of the cross-linked PPMA-based dental resins scraps was analyzed using TG/DTG to guide the operating condition. The pyrolysis was carried out in a reactor of 143 L, at 345 °C and 1.0 atmosphere. The reaction liquid products which were obtained at 30, 40, 50, 60, 70, 80, and 110 min, were physicochemically characterized for density, kinematic viscosity, and refractive index. The chemical composition of the reaction liquid products, obtained at 30, 40, 50, 60, 70, 80, and 110 min, was determined by GC-MS. The liquid phase yield was 55.50% (wt), while that of the gas phase was 31.69% (wt). The density, kinematic viscosity and refractive index of the reaction liquid products which were obtained at 30, 40, 50, 60, 70, 80, and 110 min, varied between 0.9227 and 0.9380 g/mL, 0.566 and 0.588 mm2/s, and 1.401 and 1.414, respectively. Moreover, it shows the percentage errors at the range of 0.74-2.36%, 7.40-10.86%, and 0.00-0.92%, respectively, as compared to the standard values for density, kinematic viscosity, and refractive index of pure MMA (Methyl metaclylate) at 20 °C. The GC-MS, identified in the reaction liquid products during pyrolysis, esters of carboxylic acids, alcohols, ketones, and aromatics, shows concentrations of MMA (Methyl metaclylate) between 88.003 and 98.975% (Area). The concentrations of MMA (Methyl metaclylate) in the liquid phase, between 30 and 80 min, reach purities above 98% (Area), decreasing drastically with increasing the reaction time after 100 min. Thus, it will be possible to depolymerize the cross-linked PPMA-based dental resins scraps by pyrolysis in order to recover MMA (Methyl methaclylate).
کلیدواژه ها:
نویسندگان
Paulo dos Santos Jr
UFPA, Faculty of Odontology, Belém-Brazil
Haroldo Jorge Ribeiro
UFPA, Institute of Technology, Faculty of Chemical Engineering, Belém-Brazil
Caio Ferreira
UFPA, Institute of Technology, Faculty of Chemical Engineering, Belém-Brazil
Lucas Bernar
UFPA, Institute of Technology, Faculty of Chemical Engineering, Belém-Brazil
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :